Title:
Study on surface passivation process and properties of S-130 stainless steel
Author(s):
QUAN Linlin WANG Ying
(Xi'an Space Engine Company Limited, Xi'an 710100, China)
Keywords:
S-130 stainless steel corrosion resistance polarization curve electrochemical impedance spectroscopy passivation film
PACS:
TG174.4
DOI:
-
Abstract:
In order to obtain the passivation film with excellent corrosion resistance on the surface of S-130 stainless steel(cast steel), the electrochemical workstation was used to analyze the open circuit potential curve, polarization curve(Tafel)and electrochemical impedance spectroscopy(EIS)of S-130 stainless steel in different passivation solution systems, so as to obtain the growth behavior and corrosion resistance of the passivation film.The experimental results show that the passivation film of S-130 stainless steel in citric acid system grows smoothly and the film layer is dense, and there is no dissolution phenomenon of the passivation film; after the passivation by citric acid system, the charge transfer resistance(261.4 Ω)is significantly larger than that of HNO3 passivation solution system(133.8 Ω)in 3.5% standard NaCl solution test. The corrosion current is less than that of HNO3 passivation solution system in the same environment. The corrosion current decreases by 58.4%, and the corrosion rate in NaCl solution is significantly reduced.Therefore, compared with the traditional HNO3 passivation solution, S-130 stainless steel is of better passivation effect in the new environmentally friendly citric acid passivation solution, and the passivated S-130 stainless steel also shows more excellent corrosion resistance.

References:

[1] 周金保.不锈钢的钝性和表面钝化膜工艺[J].仪表材料, 1990,21(6):371-379.
[2] 汪轩义, 吴荫顺, 张琳, 等.不锈钢钝化膜研究进展[J].材料导报, 1999, 13(3):13-14,33.
[3] 唐亚陆, 汪文兵.不锈钢柠檬酸钝化工艺研究[J].表面技术,2008,37(5):68-70.
[4] 宋凉, 刘兴斌, 叶晖.TaW10表面镀覆工艺[J].火箭推进,2009,35(1):54-58. SONG L, LIU X B, YE H.TaW10 surface plating process[J].Journal of Rocket Propulsion,2009,35(1):54-58.
[5] 任东.奥氏体和马氏体不锈钢的钝化[J].电镀与涂饰, 1996, 15(1):56-57.
[6] 杨明悦, 李雨, 刘定富.不锈钢槽体表面钝化工艺的优化[J].电镀与涂饰,2015,34(12):676-680.
[7] 曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,2008.
[8] 胡艳玲, 胡融刚, 邵敏华, 等.不锈钢钝化膜形成和破坏过程的原位ECSTM研究[J].金属学报,2001,37(9):965-970.
[9] 张胜寒, 檀玉, 梁可心.电化学阻抗谱法对304不锈钢孔蚀生长和再钝化阶段的原位研究[J].中国腐蚀与防护学报,2011,31(2):130-134.
[10] 夏浩, 周栋, 丁毅, 等.304不锈钢环保型酸洗钝化工艺及其性能研究[J].表面技术,2009,38(4):47-49.
[11] 马李洋, 丁毅, 马立群, 等.316L不锈钢柠檬酸钝化工艺及其耐点蚀性能研究[J].表面技术,2007,36(2):39-41.
[12] 任东.不锈钢钝化的新工艺[J].上海电镀, 1996(2):31-32.

Memo

Memo:
-
Last Update: 2019-06-30