新型高导电高温硫化硅橡胶研制
《火箭推进》[ISSN:1672-9374/CN:CN 61-1436/V]
卷:
42
期数:
2016年02期
页码:
64-68
栏目:
工艺与材料
出版日期:
2016-08-01
- Title:
- Development of a new high-conductivity vulcanized silicone rubber cured at high temperature
- Keywords:
- conductive filler; conductive mechanism; volume resistance
- 分类号:
- V25-34
- 文献标志码:
- A
- 摘要:
- 常规导电硅橡胶通常以硅橡胶为基胶,填充常规导电填料,通过高温硫化而成.常规导电橡胶具有导电性能、抗屏蔽性能、耐高低温性能[1].此外,导电硅橡胶还具有工艺性能良好,适宜加工结构复杂的导电橡胶制品,但是常规导电硅橡胶因其体积电阻率超过500Ω·cm,使其应用范围受到极大限制.为了研制高导电硅橡胶材料,采用甲基乙烯基硅橡胶为基胶,研究了不同导电填料对硅橡胶导电性能及力学性能影响.实验表明,当甲基乙烯基硅橡胶中填充EH200时,导电胶的导电性能最优;继续又研究了EH200添加量变化对导电胶导电性能影响,实验表明,当EH200添加30份时,导电胶体积电阻率为51Ω·cm,拉伸强度6.8MPa,综合性能优异.