卫星单组元肼发动机堵塞失效分析

《火箭推进》[ISSN:1672-9374/CN:CN 61-1436/V] 卷: 41 期数: 2015年05期 页码: 67-71 栏目: 研究与设计 出版日期: 2015-10-31
Title:
Analysis of blockage failure for monopropellant hydrazine engine in satellite
作者:
刘瀛龙; 付拓取; 陈 君; 陈 健
北京控制工程研究所，北京 100190
Author(s):
LIU Yinglong;  FU Tuoqu;  CHEN Jun;  CHEN Jian
Beijing Institute of Control Engineering, Beijing 100190, China
关键词:
单组元肼发动机; 缝隙腐蚀; 电偶腐蚀; 堵塞
Keywords:
monopropellant hydrazine engine;  crevice corrosion;  galvanic corrosion;  blockage
分类号:
V434-34
文献标志码:
A
摘要:
某型单组元肼发动机在整星AIT阶段进行专项测试检查时发现产品无喷气。针对该问题进行了故障定位、试验检测和分析。分析结果表明，导致该故障的的原因是产品经历的环境在产品内部建立了缝隙腐蚀和电偶腐蚀的条件。在长期的腐蚀效应下，生成的腐蚀产物将流体通道堵塞。
Abstract:
There was no gas exhausted from a monopropellant hydrazine engine, which was found when it was tested during AIT. The fault location, testing and analysis for this failure were carried out. The analysis results show that the reason of the failure is the environment where the thruster suffered from the crevice corrosion and the galvanic corrosion. The corrosion product which was generated by the long-term corrosion obstructed the fluid channel.

参考文献/References:

[1]周汉申. 单组元液体火箭发动机设计与研究[M]. 北京: 中国宇航出版社, 2009.
[2]朱宁昌. 液体火箭发动机设计[M]. 北京: 中国宇航出版社, 2005.
[3]杨德钧, 沈卓身. 金属腐蚀学[M]. 2版. 北京: 冶金工业出版社, 1999.
[4]刘秀晨, 安成强. 金属腐蚀学[M]. 北京: 国防工业出版社, 2002.

[5]孙跃, 胡津. 金属腐蚀与控制[M]. 哈尔滨: 哈尔滨工业大学出版社, 2003.

[6]赵麦群, 雷阿丽. 金属的腐蚀与防护[M]. 北京: 国防工业出版社, 2002.
[7]湛建阶, 陈朝辉. 肼类分解催化剂研究进展[J]. 材料导报, 2007, 21(2): 62-66.
[8]皇甫淑君. 若干金属材料局部腐蚀新现象的研究[D]. 青岛: 中国海洋大学, 2009.
[9]梁利花. 微液滴现象在大气腐蚀过程中的作用[D]. 青岛: 中国海洋大学, 2009.
[10]牛绍蕊.不锈钢的电化学腐蚀性能研究[D]. 兰州: 兰州理工大学, 2010.

备注/Memo

收稿日期：2015-06-02；修回日期：2015-07-15 作者简介：刘瀛龙（1984—），男，工程师，研究领域为空间单组元发动机

更新日期/Last Update: 1900-01-01