橡胶膜片表面喷霜成因及解决方法

《火箭推进》[ISSN:1672-9374/CN:CN 61-1436/V] 卷: 35 期数: 2009年06期页码: 41-46 栏目: 工艺与材料出版日期: 2009-12-30

Title:: Blooming of rubber diaphragm and the prevention

作者:: 马海瑞; 刘新良; 西安航天动力研究所，陕西西安 710100

Author(s):: Ma Hairui; Liu Xinliang; Xi′an Aerospace Propulsion Institute, Xi′an 710100, China

关键词:: 橡胶; 膜片; 喷霜

分类号:: TQ330.6

文献标志码:: A

摘要:: 对橡胶制品喷霜的成因从配方设计、硫化工艺、模具、环境条件、氧化影响等方面进行了理论分析，并针对橡胶膜片表面喷霜现象进行了电镜扫描测试及机理分析研究。冷却温度对膜片表面喷霜影响试验表明，膜片制造工艺过程中膜片启模后，冷却温度控制在0～15℃可有效解决膜片表面喷霜问题。

Abstract:: In this paper the reason of rubber products blooming was analyzed based on formula design, vulcanizing process, mould, environment and oxidation condition. The mechanism of rubber diaphragm blooming was studied through scanning electron microscopy(SEM). According to the experiment results, rubber diaphragm blooming can be effectively prevented by controlling the cooling temperature between 0℃ and 15℃ after the diaphragm is taken out of the mould.

参考文献/References:

[1]君轩. 喷霜[J]. 世界橡胶工业, 2004, (1): 58.
[2]杨建华, 娄诚玉. 乙丙橡胶防水片材粘接性能[J]. 中国建筑防水, 1998, (1): 20-21.
[3]吴宏晓. 力车轮胎喷霜成因及解决方法[J].橡胶工业，2000, 47(3): 168-171.
[4]张文芳, 林宜超. 运动鞋大底喷霜的能量色散X射线荧光分析[J]. 分析测试学报, 2003, 22(1): 84-85.
[5]李道力. 子午线轮胎钢丝胶帘布喷霜问题探讨[J]. 湖北化工, 2002, 6: 47-48.
[6]侯永振. 橡胶制品喷霜的原因分析及预防措施[J]. 橡塑资源利用, 2007, (1): 18-21.

备注/Memo

收稿日期：2009-07-16；修回日期：2009-08-11。
作者简介：马海瑞（1979—），男，硕士，研究领域为橡塑密封技术。

更新日期/Last Update: 1900-01-01